Monday, October 17, 2011

Cone 6 Oxidation Results Group 8

Cone 6 Oxidation Results Group 8

All of the results below for Cone 6 glazes were achieved with the use of a cooling cycle.  See the following link for details on firing and cooling schedule:
Cone 6 Oxidation Results Group 5

Links to Cone 6 Groups 1 - 4 without controlled cooling.

Group 1

Group 2

Group 3

Group 4
Links to Cone 6 Groups 1 - 4 with controlled cooling.

Group 5
Group 6

Group7
 152C
152 - Turquoise Matt Cone 6 
           
Nepheline Syenite       62%

Strontium Carbonate   21%

Silica                           8%

OM#4 Ball Clay          7%

Lithium Carbonate      3%

Copper Carbonate       4%

Bentonite                    2%



 152C over 8 - with controlled cooling.

152 - Turquoise Matt Cone 6 
           
Nepheline Syenite       62%

Strontium Carbonate  21%

Silica                           8%

OM#4 Ball Clay          7%

Lithium Carbonate      3%

Copper Carbonate       4%

Bentonite                    2%


8 - Jen's Juicy Fruit Variation (Red Matte) Cone 6   
           
EPK                            10%

Gillespie borate           9%

Nepheline syenite        49%

Flint                             12%

Whiting                       11%

Lithium carbonate       9%

Soda ash                      10%

Titanium dioxide         5%

Black Iron Oxide        6%



152 over 162 - with controlled cooling.

152 - Turquoise Matt Cone 6 
           
Nepheline Syenite       62%

Strontium Carbonate   21%

Silica                           8%

OM#4 Ball Clay          7%

Lithium Carbonate      3%

Copper Carbonate       4%

Bentonite                    2%

162 - Bailey's Red C/6 
           
Custer Feldspar           42.1%

Flint                             12.3%

EPK                            13.4%

Talc                            10.3%

Bone Ash                    13.1%

Lithium Carb               2.6%

Frit 3124                     6.2%

Red Iron Oxide           7.3%

Bentonite                    0.02


159C - with controlled cooling.

159 - Carmen's Turquoise C/6
           
Neph Syenite               52.8%

Whiting                       1.9%

Strontium Carb           30.2%

EPK                            8.5%

Flint                              6.6%

Copper Carb                4.3%

Bentonite                     3%


 159C over 77 - with controlled cooling.
 
159 - Carmen's Turquoise C/6
           
Neph Syenite               52.8%

Whiting                       1.9%

Strontium Carb           30.2%

EPK                            8.5%

Flint                              6.6%

Copper Carb                4.3%

Bentonite                     3%

77 - Ron Roy Raw Sienna C/6  
           
Frit 3195                     23%

Wollastonite                28%

Neph Syenite              4%

EPK                            28%

Silica                          17%

Rutile                          6%

Red Iron Oxide           6%


161C over 43 - with controlled cooling. 

161 - Apricot C/6       
           
Custer Spar     44%

Whiting           19.9%

Flint                 10.7%

EPK                10.7%

Lithium Carb   5.3%

Talc                 3.1%

Frit 3124         6.4%

Rutile              7%

Bentonite        2%


43 - Kaki with Gillespie Borate C/6  
           
Gillespie Borate          27%

Flint                             25.3%

Custer Spar                 16.9%

Talc                             11.8%

EPK                            4.2%

Red Iron Oxide           12.8%

Bentonite                    2%



161C over 72 - with controlled cooling.


161 - Apricot C/6       
           
Custer Spar     44%

Whiting           19.9%

Flint                 10.7%

EPK                10.7%

Lithium Carb   5.3%

Talc                 3.1%

Frit 3124         6.4%

Rutile              7%

Bentonite        2%


72 – Ron Roy Waterfall Brown C/6  
           
Frit 3134                     33.5%

Frit 3195                     26%

OM4 Ball Clay            17%

Silica                           23.5%

Red Iron Oxide           12.5%

Rutile                          .1%

162 C - with controlled cooling.
162 - Bailey's Red C/6           
           
Custer Feldspar           42.1%

Flint                             12.3%

EPK                            13.4%

Talc                             10.3%

Bone Ash                    13.1%

Lithium Carb               2.6%

Frit 3124                     6.2%

Red Iron Oxide           7.3%

Bentonite                    2%


 163C - with controlled cooling.

 163C -with controlled cooling, thicker application than above.

163 - Red Orange C/6
           
Minspar           47.7%

Talc                 17.2%

Bone Ash        15.3%

Flint                 11.6%

EPK                4.1%

Lithium Carb   4.1%

Crocus martis  11.5%

Bentonite        2%



 169C -with controlled cooling.

169 - DJ's Perfect Purple Cone 6       
           
Neph Syenite              18%

Frit 3134                     14%

Whiting                       20%

OM 4                           18%

Silica                           3%

Chrome Ox                 .02%

Tin Oxide                    7.5%

Cobalt Carb                 1%

Red Iron Oxide           5%


 169C over 87 - with controlled cooling.

169 - DJ's Perfect Purple Cone 6       
           
Neph Syenite              18%

Frit 3134                     14%

Whiting                       20%

OM 4                           18%

Silica                           30%

Chrome Ox                 .2%

Tin Oxide                    7.5%

Cobalt Carb                 1%

Red Iron Oxide           5%


87 - Zinc Semimatte/Glossy Base Glaze Sea Green C/6       
           
Neph Syenite              36%

Wollastonite                13%

Zinc Oxide                  10%

EPK                            10%

Silica                           31%

Cobalt Carbonate        1%

Rutile                          6%


 171C - with controlled cooling.

171 - Lana Purple C/6 Semi-matte     
           
Custer Spar                 27.2%

Frit 3134                     8.2%

Silica                           31.8%

Whiting                       11.7%

Neph Sye                    14%

Strontium Carb           3.5%

Magnesium Carb        1.6%

Bentonite                    2%

Cobalt Carb                 0.6%

Tin Oxide                    4.8%

Chromium Oxide        0.2%


 171C over 87 - with controlled cooling.


171 - Lana Purple C/6 Semi-matte     
           
Custer Spar                 27.2%

Frit 3134                     8.2%

Silica                           31.8%

Whiting                       11.7%

Neph Sye                    14%

Strontium Carb           3.5%

Magnesium Carb        1.6%

Bentonite                    2%

Cobalt Carb                 0.6%

Tin Oxide                    4.8%

Chromium Oxide        0.2%


87 - Zinc Semimatte/Glossy Base Glaze Sea Green C/6       
           
Neph Syenite              36%

Wollastonite                13%

Zinc Oxide                  10%

EPK                            10%

Silica                           31%

Cobalt Carbonate        1%

Rutile                          6%

 176C - without controlled cooling.

176 - Pinnell Green Black C/6           
           
Frit 3134              4.3%

Neph Syenite       29.3%

Spodumene          27.2%

Strontium Carb    17.8%

EPK                    12%

Silica                   8%

Titanium Dioxide  5%

Copper Carb        5%


 177C - with controlled cooling.

177C - Bailey's Blue C/6       
           
Minspar           43%

EPK                5%

Silica               21.5%

Zinc Oxide      6%

Whiting           22.5%

Bentonite        2%

Cobalt Oxide  3%

 177C over 87 - with controlled cooling.

177C - Bailey's Blue C/6       
           
Minspar           43%

EPK                5%

Silica               21.5%

Zinc Oxide      6%

Whiting           22.5%

Bentonite        2%

Cobalt Oxide  3%


87 - Zinc Semimatte/Glossy Base Glaze Sea Green C/6       
           
Neph Syenite              36%

Wollastonite                13%

Zinc Oxide                  10%

EPK                            10%

Silica                           31%

Cobalt Carbonate        1%

Rutile                          6%





































 

Sunday, October 16, 2011

Cone 6 Oxidation Results Group 7

Cone 6 Oxidation Results Group 7

All of the results below for Cone 6 glazes were achieved with the use of a cooling cycle.  See the following link for details on firing and cooling schedule:
Cone 6 Oxidation Results Group 5

Links to Cone 6 Groups 1 - 4 without controlled cooling.

Group 1

Group 2

Group 3

Group 4




 Link to Cone 6 Group 6 with controlled cooling.



72C with controlled cooling.
72 -  Ron Roy Waterfall Brown C/6  
           
Frit 3134                     33.5%

Frit 3195                     26%

OM4 Ball Clay            17%

Silica                           23.5%

Red Iron Oxide           12.5%

Rutile                          .1%
 

75C with controlled cooling.
75 – Ron Roy High Calcium Semimatte Base 2 C/6 
           
Frit 3195         23%

Wollastonite    28%

Neph Syenite  4%

EPK                28%

Silica               17%

Copper Carb    5%

Rutile              6%



 77C with controlled cooling.

77 – Ron Roy Raw Sienna C/6          
           
Frit 3195                    23%

Wollastonite                28%

Neph Syenite              4%

EPK                            28%

Silica                           17%

Rutile                          6%

Red Iron Oxide           6%

 77 - without controlled cooling.


78C - with controlled cooling.

78 – Ron Roy Spearmint C/6 
           
Frit 3195           23%

Wollastonite      28%

Neph Syenite     4%

EPK                    28%

Silica                 17%

Rutile                 6%

Copper Carb     4%


87C

87 – Ron Roy Zinc Semimatt Sea Green C/6   
           
Neph Syenite              36%

Wollastonite                13%

Zinc Oxide                  10%

EPK                            10%

Silica                          31%

Cobalt Carbonate        1%

Rutile                          6%



87C over 70 - with controlled cooling.

87 – Ron Roy Zinc Semimatt Sea Green C/6   
           
Neph Syenite              36%

Wollastonite                13%

Zinc Oxide                  10%

EPK                            10%

Silica                           31%

Cobalt Carbonate        1%

Rutile                          6%

70 - Raspberry C/6      
Whiting                       20%
Neph Syenite              18%

Frit 3134                      14%

Om-4 Ball Clay           18%

Silica                           30%

Green Chrome Ox       .02%

Tin Oxide                    7.5%


 87C over 169 - with controlled cooling.
 
87 – Ron Roy Zinc Semimatt Sea Green C/6   
           
Neph Syenite              36%

Wollastonite                13%

Zinc Oxide                  10%

EPK                            10%

Silica                           31%

Cobalt Carbonate        1%

Rutile                          6%

169 - DJ's Perfect Purple Cone 6        
           
Neph Syenite        18%          

Frit 3134               14%          

Whiting         20%

OM 4                     18%          

Silica               30%

Chrome Ox           .2%        

Tin Oxide              7.5%        

Cobalt Carb           1%           
Red Iron Oxide   5%         


87C over 171 - with controlled cooling.
                                                       

87 – Ron Roy Zinc Semimatt Sea Green C/6   
           
Neph Syenite              36%

Wollastonite                13%

Zinc Oxide                  10%

EPK                            10%

Silica                           31%

Cobalt Carbonate        1%

Rutile                          6%

171 - Lana Purple C/6 Semi-matte     
           
Custer Spar                 27.2%

Frit 3134                     8.2%

Silica                           31.8%

Whiting                       11.7%

Neph Sye                    14%

Strontium Carb           3,5%

Magnesium Carb         1.6%

Bentonite                    2.%

Cobalt Carb                 .6%

Tin Oxide                    4.8%
Chromium Oxide        .2% 


 100C - with controlled cooling.



100 - Bronze Green Matt glaze C/6   
           
Lithium Carb               1%

Strontium Carb           20%

Neph Syenite              60%

Ball Clay                     10%

Silica                           9%

Titanium Dioxide        5%

Copper carb                 5%


118C - with controlled cooling

118 - Transparent - C/6 Yellow    

Minspar           37.3%

Bentonite        2%

Dolomite         6.6%

Lithium Carb   3.7%

Whiting           11.8%

Zinc Oxide      4.1%

Silica               34.5%

Yellow Stain Standard's K83       10%
 

132C - with controlled cooling.


132 - Blue Green Sugar Maples Cone 6        

Talc                             3.3%

Whiting                       14.3%

Frit 3134                     13.3%

Minspar                       46.2%

EPK                            6.4%

Silica                          16.5%

Tin Oxide                    2.4%

Zinc Oxide                  4.4%

Black Copper Ox        1.1%

Bentonite                    2%



 132C over 71 - with controlled cooling.

132 - Blue Green Sugar Maples Cone 6        

Talc                             3.3%

Whiting                       14.3%

Frit 3134                     13.3%

Minspar                       46.2%

EPK                            6.4%

Silica                          16.5%

Tin Oxide                    2.4%

Zinc Oxide                  4.4%

Black Copper Ox        1.1%

Bentonite                    2%


71 – Ron Roy Waxwing Brown C/6 
           
Frit 3134                     34.5%

Talc                             9.5%

OM4 Ball Clay            25%

Silica                           31%

Red Iron Oxide           15%

Titanium Dioxide        .15%



 132C over 118 - with controlled cooling.

132 - Blue Green Sugar Maples Cone 6        

Talc                             3.3%

Whiting                       14.3%

Frit 3134                     13.3%

Minspar                       46.2%

EPK                            6.4%

Silica                          16.5%

Tin Oxide                    2.4%

Zinc Oxide                  4.4%

Black Copper Ox        1.1%

Bentonite                    2%


118 - Transparent - C/6 Yellow    

Minspar           37.3%

Bentonite        2%

Dolomite         6.6%

Lithium Carb   3.7%

Whiting           11.8%

Zinc Oxide      4.1%

Silica               34.5%

Yellow Stain Standard's K83       10%



 137C - with controlled cooling.


137 - Oribe Green Cone 6 Sugar Maples       

Custer Spar     32%

Whiting           24%

Silica               24%

EPK                12%

Zinc Oxide      8%

Copper Carb    5%

Bentonite        2%



 138C - with controlled cooling.

138 - Faux Celedon Cone 6 Sugar Maples    
           
Minspar           41%

Silica               19%

Zircopax          12%

Whiting           7%

Dolomite         5%

Zinc Oxide      2%

Kent. #4 Ball Clay      1%

Copper Carb    2.5%

Bentonite        2%


143C - with controlled cooling. 

143 - Hansen Clear GA12 Cone 6 Darker Green      
           
Custer Spar     20%

Frit 3134         20%

EPK               20%

Wollastonite    20%

Silica               20%

Copper Carb    4%

Bentonite        2%


143C over 17 - with controlled cooling.
143 - Hansen Clear GA12 Cone 6 Darker Green      
           
Custer Spar     20%

Frit 3134         20%

EPK               20%

Wollastonite    20%

Silica               20%

Copper Carb    4%

Bentonite        2%

17 - Randy's Red C 5/6         
           
Flint                             30%

EPK                           5%

G200                           20%

Talc                             15%

Gillespie Borate          30%

Red Iron Oxide           15%

 145C - with controlled cooling.

 
145 - Satin Matt Cone 6 Lt. Green    
           
Neph Syenite              41.8%
Gillespie Borate          10.4%
EPK                            12.5%
Whiting                       10.4%
Lithium Carb               6.2%
Silica                           12.5%
Titanium Dioxide        6.2%
Copper Carb                2%
Bentonite                     2%


 147C - with controlled cooling.

147 - Satin Matt Cone 6 Rusty Bronze
           
Neph Syenite              41.8%

Gillespie Borate          10.4%

EPK                            12.5%

Whiting                       10.4%

Lithium Carb               6.2%

Silica                           12.5%

Titanium Dioxide        6.2%

Red Iron Oxide           3%