Cone 6 Oxidation Results Group 8
All of the results below for Cone 6 glazes were achieved with the use of a cooling cycle. See the following link for details on firing and cooling schedule:
Cone 6 Oxidation Results Group 5
Links to Cone 6 Groups 1 - 4 without controlled cooling.
Group 1
Group 2
Group 3
Group 4
Links to Cone 6 Groups 1 - 4 with controlled cooling.
Group 5
Group 6
Group7
152C
152 - Turquoise Matt Cone 6
Nepheline Syenite 62%
Strontium Carbonate 21%
Silica 8%
OM#4 Ball Clay 7%
Lithium Carbonate 3%
Copper Carbonate 4%
Bentonite 2%
152C over 8 - with controlled cooling.
152 - Turquoise Matt Cone 6
Nepheline Syenite 62%
Strontium Carbonate 21%
Silica 8%
OM#4 Ball Clay 7%
Lithium Carbonate 3%
Copper Carbonate 4%
Bentonite 2%
8 - Jen's Juicy Fruit Variation (Red Matte) Cone 6
EPK 10%
Gillespie borate 9%
Nepheline syenite 49%
Flint 12%
Whiting 11%
Lithium carbonate 9%
Soda ash 10%
Titanium dioxide 5%
Black Iron Oxide 6%
152 over 162 - with controlled cooling.
152 - Turquoise Matt Cone 6
Nepheline Syenite 62%
Strontium Carbonate 21%
Silica 8%
OM#4 Ball Clay 7%
Lithium Carbonate 3%
Copper Carbonate 4%
Bentonite 2%
162 - Bailey's Red C/6
Custer Feldspar 42.1%
Flint 12.3%
EPK 13.4%
Talc 10.3%
Bone Ash 13.1%
Lithium Carb 2.6%
Frit 3124 6.2%
Red Iron Oxide 7.3%
Bentonite 0.02
159C - with controlled cooling.
159 - Carmen's Turquoise C/6
Neph Syenite 52.8%
Whiting 1.9%
Strontium Carb 30.2%
EPK 8.5%
Flint 6.6%
Copper Carb 4.3%
Bentonite 3%
159C over 77 - with controlled cooling.
159 - Carmen's Turquoise C/6
Neph Syenite 52.8%
Whiting 1.9%
Strontium Carb 30.2%
EPK 8.5%
Flint 6.6%
Copper Carb 4.3%
Bentonite 3%
77 - Ron Roy Raw Sienna C/6
Frit 3195 23%
Wollastonite 28%
Neph Syenite 4%
EPK 28%
Silica 17%
Rutile 6%
Red Iron Oxide 6%
161C over 43 - with controlled cooling.
161 - Apricot C/6
Custer Spar 44%
Whiting 19.9%
Flint 10.7%
EPK 10.7%
Lithium Carb 5.3%
Talc 3.1%
Frit 3124 6.4%
Rutile 7%
Bentonite 2%
43 - Kaki with Gillespie Borate C/6
Gillespie Borate 27%
Flint 25.3%
Custer Spar 16.9%
Talc 11.8%
EPK 4.2%
Red Iron Oxide 12.8%
Bentonite 2%
161C over 72 - with controlled cooling.
161 - Apricot C/6
Custer Spar 44%
Whiting 19.9%
Flint 10.7%
EPK 10.7%
Lithium Carb 5.3%
Talc 3.1%
Frit 3124 6.4%
Rutile 7%
Bentonite 2%
72 – Ron Roy Waterfall Brown C/6
Frit 3134 33.5%
Frit 3195 26%
OM4 Ball Clay 17%
Silica 23.5%
Red Iron Oxide 12.5%
Rutile .1%
162 C - with controlled cooling.
162 - Bailey's Red C/6
Custer Feldspar 42.1%
Flint 12.3%
EPK 13.4%
Talc 10.3%
Bone Ash 13.1%
Lithium Carb 2.6%
Frit 3124 6.2%
Red Iron Oxide 7.3%
Bentonite 2%
163C - with controlled cooling.
163C -with controlled cooling, thicker application than above.
163 - Red Orange C/6
Minspar 47.7%
Talc 17.2%
Bone Ash 15.3%
Flint 11.6%
EPK 4.1%
Lithium Carb 4.1%
Crocus martis 11.5%
Bentonite 2%
169C -with controlled cooling.
169 - DJ's Perfect Purple Cone 6
Neph Syenite 18%
Frit 3134 14%
Whiting 20%
OM 4 18%
Silica 3%
Chrome Ox .02%
Tin Oxide 7.5%
Cobalt Carb 1%
Red Iron Oxide 5%
169C over 87 - with controlled cooling.
169 - DJ's Perfect Purple Cone 6
Neph Syenite 18%
Frit 3134 14%
Whiting 20%
OM 4 18%
Silica 30%
Chrome Ox .2%
Tin Oxide 7.5%
Cobalt Carb 1%
Red Iron Oxide 5%
87 - Zinc Semimatte/Glossy Base Glaze Sea Green C/6
Neph Syenite 36%
Wollastonite 13%
Zinc Oxide 10%
EPK 10%
Silica 31%
Cobalt Carbonate 1%
Rutile 6%
171C - with controlled cooling.
171 - Lana Purple C/6 Semi-matte
Custer Spar 27.2%
Frit 3134 8.2%
Silica 31.8%
Whiting 11.7%
Neph Sye 14%
Strontium Carb 3.5%
Magnesium Carb 1.6%
Bentonite 2%
Cobalt Carb 0.6%
Tin Oxide 4.8%
Chromium Oxide 0.2%
171C over 87 - with controlled cooling.
171 - Lana Purple C/6 Semi-matte
Custer Spar 27.2%
Frit 3134 8.2%
Silica 31.8%
Whiting 11.7%
Neph Sye 14%
Strontium Carb 3.5%
Magnesium Carb 1.6%
Bentonite 2%
Cobalt Carb 0.6%
Tin Oxide 4.8%
Chromium Oxide 0.2%
87 - Zinc Semimatte/Glossy Base Glaze Sea Green C/6
Neph Syenite 36%
Wollastonite 13%
Zinc Oxide 10%
EPK 10%
Silica 31%
Cobalt Carbonate 1%
Rutile 6%
176C - without controlled cooling.
176 - Pinnell Green Black C/6
Frit 3134 4.3%
Neph Syenite 29.3%
Spodumene 27.2%
Strontium Carb 17.8%
EPK 12%
Silica 8%
Titanium Dioxide 5%
Copper Carb 5%
177C - with controlled cooling.
177C - Bailey's Blue C/6
Minspar 43%
EPK 5%
Silica 21.5%
Zinc Oxide 6%
Whiting 22.5%
Bentonite 2%
Cobalt Oxide 3%
177C over 87 - with controlled cooling.
177C - Bailey's Blue C/6
Minspar 43%
EPK 5%
Silica 21.5%
Zinc Oxide 6%
Whiting 22.5%
Bentonite 2%
Cobalt Oxide 3%
87 - Zinc Semimatte/Glossy Base Glaze Sea Green C/6
Neph Syenite 36%
Wollastonite 13%
Zinc Oxide 10%
EPK 10%
Silica 31%
Cobalt Carbonate 1%
Rutile 6%